CYCOLOY PC/ABS CY6110，CY6110物性表，SABIC，沙伯基础创新塑料有限公司
CYCOLOY™ FR Resin CY6110 - Asia
聚碳酸酯+丙烯腈丁二烯苯乙烯
SABIC
Product Description:
CYCOLOY CY6110 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an impact modified, high flow injection moldable, non chlorinated/brominated flame retardant grade. It features good hydrostability and has a UL94 V0@1.5mm and 5VB@2.5mm flame rating.
点击下载CYCOLOY CY6110物性表：
聚碳酸酯+丙烯腈丁二烯苯乙烯
SABIC
Product Description:
CYCOLOY CY6110 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an impact modified, high flow injection moldable, non chlorinated/brominated flame retardant grade. It features good hydrostability and has a UL94 V0@1.5mm and 5VB@2.5mm flame rating.
|
用途
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度
|
1.18
|
g/cm³
|
ISO 1183 |
|
熔融体积流量（MVR） (260°C/2.16 kg)
|
23
|
cm³/10min
|
ISO 1133 |
|
收缩率 - 流动 (3.20 mm)
|
0.40 到 0.60
|
%
|
内部方法 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.60
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.20
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 1
|
2760
|
MPa
|
ASTM D638 |
|
--
|
2750
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 2
|
63.0
|
MPa
|
ASTM D638 |
|
屈服
|
63.0
|
MPa
|
ISO 527-2/50 |
|
断裂 2
|
47.0
|
MPa
|
ASTM D638 |
|
断裂
|
46.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服 2
|
4.1
|
%
|
ASTM D638 |
|
屈服
|
4.0
|
%
|
ISO 527-2/50 |
|
断裂 2
|
65
|
%
|
ASTM D638 |
|
断裂
|
35
|
%
|
ISO 527-2/50 |
|
弯曲模量 3
|
2440
|
MPa
|
ISO 178 |
|
弯曲应力 3, 4
|
94.0
|
MPa
|
ISO 178 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度
|
ISO 179/1eA | ||
|
-30°C 5
|
10
|
kJ/m²
|
|
|
23°C 5
|
45
|
kJ/m²
|
|
|
23°C 6
|
33
|
kJ/m²
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
100
|
J/m
|
ASTM D256 |
|
23°C
|
480
|
J/m
|
ASTM D256 |
|
-30°C 7
|
10
|
kJ/m²
|
ISO 180/1A |
|
-30°C 8
|
12
|
kJ/m²
|
ISO 180/1A |
|
23°C 7
|
45
|
kJ/m²
|
ISO 180/1A |
|
23°C 8
|
25
|
kJ/m²
|
ISO 180/1A |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度 8
|
|||
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距
|
98.0
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距
|
88.0
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
106
|
°C
|
ISO 306/B120 |
|
--
|
104
|
°C
|
ISO 306/B50 |
|
Ball Pressure Test (73 到 77°C)
|
通过
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
ISO 11359-2 | ||
|
流动 : -40 到 40°C
|
8.0
|
cm/cm/°C
|
|
|
垂直 : -40°C
|
8.0
|
cm/cm/°C
|
|
|
RTI Elec
|
85.0
|
°C
|
UL 746 |
|
RTI Imp
|
85.0
|
°C
|
UL 746 |
|
RTI
|
85.0
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+15
|
ohms
|
IEC 60093 |
|
体积电阻率
|
1.0E+15
|
ohms·cm
|
IEC 60093 |
|
介电强度
|
IEC 60243-1 | ||
|
0.800 mm, 在油中
|
46
|
kV/mm
|
|
|
1.60 mm, 在油中
|
31
|
kV/mm
|
|
|
相对电容率
|
IEC 60250 | ||
|
50 Hz
|
2.90
|
|
|
|
60 Hz
|
2.90
|
|
|
|
1 MHz
|
2.90
|
|
|
|
耗散因数
|
IEC 60250 | ||
|
50 Hz
|
2.0E-3
|
|
|
|
60 Hz
|
2.0E-3
|
|
|
|
1 MHz
|
7.0E-3
|
|
|
|
相比耐漏电起痕指数(CTI)
|
PLC 0
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 3
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
1.5 mm
|
V-0
|
|
|
|
2.5 mm
|
5VB
|
|
|
|
灼热丝易燃指数 (1.0 mm)
|
960
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度
|
IEC 60695-2-13 | ||
|
1.0 mm
|
825
|
°C
|
|
|
2.0 mm
|
825
|
°C
|
|
|
3.0 mm
|
825
|
°C
|
|
|
极限氧指数
|
31
|
%
|
ISO 4589-2 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
80 到 90
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料斗温度
|
60 到 80
|
°C
|
|
|
料筒后部温度
|
230 到 280
|
°C
|
|
|
料筒中部温度
|
240 到 290
|
°C
|
|
|
料筒前部温度
|
250 到 300
|
°C
|
|
|
射嘴温度
|
250 到 300
|
°C
|
|
|
加工（熔体）温度
|
250 到 300
|
°C
|
|
|
模具温度
|
60 到 85
|
°C
|
|
|
排气孔深度
|
0.030 到 0.075
|
mm
|
| 备注 |
| 15.0 mm/min |
| 2类型 1, 50 mm/min |
| 32.0 mm/min |
| 4at Yield |
| 580*10*3 sp=62mm |
| 680*10*4 sp=62mm |
| 780*10*3 mm |
| 880*10*4 mm |
点击下载CYCOLOY CY6110物性表：
备注：以上数据表中的信息由 HuasuStar - 华塑之星 从该材料的生产商处获得。HuasuStar - 华塑之星 尽最大努力确保此数据的准确性。 但是 HuasuStar - 华塑之星 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料生产商进行验证。
如需购买此材料，请联系我们：0769-87796856 huasu@huasustar.com