XENOY HX5600HP|PC/PBT HX5600HP|沙特基础工业公司|XENOY HX5600HP物性表|HX5600HP PBT塑胶原料|SABIC代理商
XENOY™ Resin HX5600HP - Asia
聚碳酸酯+PBT
SABIC
Product Description:
Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.
点击下载XENOYHX5600HP物性表：
聚碳酸酯+PBT
SABIC
Product Description:
Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.
|
用途
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.22
|
g/cm³
|
ASTM D792, ISO 1183 |
|
熔流率（熔体流动速率） (250°C/5.0 kg)
|
11
|
g/10 min
|
ASTM D1238 |
|
熔融体积流量（MVR） (250°C/5.0 kg)
|
10
|
cm³/10min
|
ISO 1133 |
|
收缩率 - 流动 (3.20 mm)
|
0.70 到 1.1
|
%
|
内部方法 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.40
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.050
|
%
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 1
|
2100
|
MPa
|
ASTM D638 |
|
--
|
2050
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 2
|
50.0
|
MPa
|
ASTM D638 |
|
屈服
|
50.0
|
MPa
|
ISO 527-2/50 |
|
断裂 2
|
52.0
|
MPa
|
ASTM D638 |
|
断裂
|
55.0
|
MPa
|
ISO 527-2/50 |
|
伸长率
|
|||
|
屈服 2
|
5.0
|
%
|
ASTM D638 |
|
屈服
|
5.0
|
%
|
ISO 527-2/50 |
|
断裂 2
|
150
|
%
|
ASTM D638 |
|
断裂
|
100
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 3
|
2000
|
MPa
|
ASTM D790 |
|
-- 4
|
2050
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
-- 4, 5
|
75.0
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 3
|
70.0
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 6 (23°C)
|
60
|
kJ/m²
|
ISO 179/1eA |
|
简支梁无缺口冲击强度 7 (-30°C)
|
无断裂
|
|
ISO 179/1eU |
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
600
|
J/m
|
ASTM D256 |
|
23°C
|
750
|
J/m
|
ASTM D256 |
|
-30°C 8
|
25
|
kJ/m²
|
ISO 180/1A |
|
23°C 8
|
55
|
kJ/m²
|
ISO 180/1A |
|
无缺口伊佐德冲击强度 8 (-40°C)
|
无断裂
|
|
ISO 180/1U |
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
80.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
|
105
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
80.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
|
80.0
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
125
|
°C
|
ASTM D1525 9, ISO 306/B50 9 |
|
--
|
123
|
°C
|
ISO 306/B120 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
9.0E-5
|
cm/cm/°C
|
ASTM E831, ISO 11359-2 |
|
流动 : 23 到 60°C
|
1.0E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : -40 到 40°C
|
9.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -40°C
|
9.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
| 充模分析 |
额定值
|
单位制
|
测试方法
|
|
熔体粘度 (260°C, 1500 sec^-1)
|
260
|
Pa·s
|
ISO 11443 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
90 到 100
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料斗温度
|
40 到 60
|
°C
|
|
|
料筒后部温度
|
230 到 250
|
°C
|
|
|
料筒中部温度
|
240 到 265
|
°C
|
|
|
料筒前部温度
|
250 到 270
|
°C
|
|
|
射嘴温度
|
250 到 265
|
°C
|
|
|
加工（熔体）温度
|
255 到 270
|
°C
|
|
|
模具温度
|
60 到 80
|
°C
|
| 备注 |
| 15.0 mm/min |
| 2类型 1, 50 mm/min |
| 31.3 mm/min |
| 42.0 mm/min |
| 5at Yield |
| 680*10*4 sp=62mm |
| 780*10*3 sp=62mm |
| 880*10*4 mm |
| 9速率 A (50°C/h), 载荷2 (50N) |
点击下载XENOYHX5600HP物性表：
备注：以上数据表中的信息由 HuasuStar - 华塑之星 从该材料的生产商处获得。HuasuStar - 华塑之星 尽最大努力确保此数据的准确性。 但是 HuasuStar - 华塑之星 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料生产商进行验证。
如需购买此材料，请联系我们：0769-87796856 huasu@huasustar.com
塑料行业新闻动态
-
2024-01-08
地址
电话：0769- 3388 3988
邮箱： huasu@huasustar.com
联系
东莞市华塑之星新材料科技有限公司
办公地址: 广东省 东莞市 松山湖 研发五路2号宏远新智汇
工厂地址: 广东省 东莞市 樟木头 镇沿河路5号东基产业园