VALOX HX420HP|PBT HX420HP|沙特基础工业公司|VALOX HX420HP物性表|HX420HP PBT塑胶原料|SABIC代理商
VALOX™ Resin HX420HP - Americas
聚丁烯对苯二甲酸酯
SABIC
Product Description:
30% Glass Reinforced PBT resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), US FDA food contact compliant, gamma, e-beam, EtO sterilizable. Available in limited colors.
点击下载VALOXHX420HP物性表：
聚丁烯对苯二甲酸酯
SABIC
Product Description:
30% Glass Reinforced PBT resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), US FDA food contact compliant, gamma, e-beam, EtO sterilizable. Available in limited colors.
|
用途
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.53
|
g/cm³
|
ASTM D792, ISO 1183 |
|
特定体积
|
0.660
|
cm³/g
|
ASTM D792 |
|
熔流率（熔体流动速率） (250°C/2.16 kg)
|
17
|
g/10 min
|
ASTM D1238 |
|
熔融体积流量（MVR） (250°C/2.16 kg)
|
13
|
cm³/10min
|
ISO 1133 |
|
收缩率
|
内部方法 | ||
|
垂直 : 1.50 到 3.20 mm
|
0.40 到 0.60
|
%
|
|
|
流动 : 1.50 到 3.20 mm
|
0.30 到 0.50
|
%
|
|
|
流动 : 3.20 mm
|
0.30 到 0.80
|
%
|
|
|
垂直 : 3.20 到 4.60 mm
|
0.60 到 0.90
|
%
|
|
|
流动 : 3.20 到 4.60 mm
|
0.50 到 0.80
|
%
|
|
|
吸水率
|
|||
|
24 hr
|
0.060
|
%
|
ASTM D570 |
|
饱和, 23°C
|
0.26
|
%
|
ISO 62 |
|
平衡, 23°C, 50% RH
|
0.060
|
%
|
ISO 62 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度 (R 级)
|
118
|
|
ASTM D785 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 1
|
9300
|
MPa
|
ASTM D638 |
|
--
|
9300
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 2
|
120
|
MPa
|
ASTM D638 |
|
屈服
|
125
|
MPa
|
ISO 527-2/5 |
|
断裂 2
|
120
|
MPa
|
ASTM D638 |
|
断裂
|
125
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服 2
|
3.0
|
%
|
ASTM D638 |
|
屈服
|
2.0
|
%
|
ISO 527-2/5 |
|
断裂 2
|
3.0
|
%
|
ASTM D638 |
|
断裂
|
2.0
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 3
|
7580
|
MPa
|
ASTM D790 |
|
-- 4
|
8500
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
-- 4, 5
|
195
|
MPa
|
ISO 178 |
|
断裂, 50.0 mm 跨距 3
|
189
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度 6 (23°C)
|
5.0
|
kJ/m²
|
ISO 179/1eA |
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
80
|
J/m
|
ASTM D256 |
|
23°C
|
85
|
J/m
|
ASTM D256 |
|
-30°C 7
|
7.0
|
kJ/m²
|
ISO 180/1A |
|
23°C 7
|
8.0
|
kJ/m²
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
23°C
|
800
|
J/m
|
ASTM D4812 |
|
-30°C 7
|
45
|
kJ/m²
|
ISO 180/1U |
|
23°C 7
|
45
|
kJ/m²
|
ISO 180/1U |
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
10.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 6.40 mm
|
215
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
207
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7
|
200
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
215
|
°C
|
ASTM D1525 8, ISO 306/B50 8 |
|
--
|
220
|
°C
|
ISO 306/B120 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
2.5E-5
|
cm/cm/°C
|
ASTM E831, ISO 11359-2 |
|
流动 : 60 到 138°C
|
2.5E-5
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -40°C
|
1.2E-4
|
cm/cm/°C
|
ISO 11359-2 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
> 3.2E+16
|
ohms·cm
|
ASTM D257 |
|
介电强度
|
ASTM D149 | ||
|
1.60 mm, in Oil
|
25
|
kV/mm
|
|
|
3.20 mm, in Air
|
19
|
kV/mm
|
|
|
介电常数
|
ASTM D150 | ||
|
100 Hz
|
3.80
|
|
|
|
1 MHz
|
3.70
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
100 Hz
|
2.0E-3
|
|
|
|
1 MHz
|
0.020
|
|
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
120
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 80
|
%
|
|
|
料筒后部温度
|
240 到 255
|
°C
|
|
|
料筒中部温度
|
245 到 260
|
°C
|
|
|
料筒前部温度
|
250 到 265
|
°C
|
|
|
射嘴温度
|
245 到 260
|
°C
|
|
|
加工（熔体）温度
|
250 到 265
|
°C
|
|
|
模具温度
|
65 到 90
|
°C
|
|
|
背压
|
0.300 到 0.700
|
MPa
|
|
|
螺杆转速
|
50 到 80
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.038
|
mm
|
|
| 注射说明 | |||
|
Injection Molding Parameters
|
|||
| 备注 |
| 15.0 mm/min |
| 2类型 1, 5.0 mm/min |
| 31.3 mm/min |
| 42.0 mm/min |
| 5at Yield |
| 680*10*4 sp=62mm |
| 780*10*4 mm |
| 8速率 A (50°C/h), 载荷2 (50N) |
点击下载VALOXHX420HP物性表：
备注：以上数据表中的信息由 HuasuStar - 华塑之星 从该材料的生产商处获得。HuasuStar - 华塑之星 尽最大努力确保此数据的准确性。 但是 HuasuStar - 华塑之星 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料生产商进行验证。
如需购买此材料，请联系我们：0769-87796856 huasu@huasustar.com
塑料行业新闻动态
-
2024-12-31
地址
电话：0769- 3388 3988
邮箱： huasu@huasustar.com
联系
东莞市华塑之星新材料科技有限公司
办公地址: 广东省 东莞市 松山湖 研发五路2号宏远新智汇4栋1604