VALOX VX5022|PBT VX5022|沙特基础工业公司|VALOX VX5022物性表|VX5022 PBT塑胶原料|SABIC代理商
VALOX™ Resin VX5022 - Europe
聚丁烯对苯二甲酸酯
SABIC
Product Description:
VALOX VX5022 is a 20% glass fibre reinforced PBT+PC blend with low warpage characteristics. This grade is 5021 with reduced warpage.
点击下载VALOXVX5022物性表：
聚丁烯对苯二甲酸酯
SABIC
Product Description:
VALOX VX5022 is a 20% glass fibre reinforced PBT+PC blend with low warpage characteristics. This grade is 5021 with reduced warpage.
|
用途
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.39
|
g/cm³
|
ASTM D792, ISO 1183 |
|
熔流率（熔体流动速率）
|
ASTM D1238 | ||
|
250°C/2.16 kg
|
16
|
g/10 min
|
|
|
265°C/5.0 kg
|
50
|
g/10 min
|
|
|
266°C/5.0 kg
|
50
|
g/10 min
|
|
|
熔融体积流量（MVR）
|
ISO 1133 | ||
|
250°C/2.16 kg
|
13
|
cm³/10min
|
|
|
250°C/5.0 kg
|
28
|
cm³/10min
|
|
|
265°C/5.0 kg
|
40
|
cm³/10min
|
|
|
收缩率
|
内部方法 | ||
|
垂直 2
|
0.50 到 0.90
|
%
|
|
|
流动 2
|
0.30 到 0.80
|
%
|
|
|
流动 : 3.20 mm
|
0.30 到 0.50
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
0.10
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.060
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度 (R 计秤)
|
122
|
|
ISO 2039-2 |
|
球压硬度 (H 358/30)
|
205
|
MPa
|
ISO 2039-1 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 3
|
7300
|
MPa
|
ASTM D638 |
|
--
|
7100
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 4
|
125
|
MPa
|
ASTM D638 |
|
屈服
|
110
|
MPa
|
ISO 527-2/5 |
|
断裂 4
|
125
|
MPa
|
ASTM D638 |
|
断裂
|
110
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服 4
|
3.0
|
%
|
ASTM D638 |
|
屈服
|
3.0
|
%
|
ISO 527-2/5 |
|
断裂 4
|
3.0
|
%
|
ASTM D638 |
|
断裂
|
3.0
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 5
|
5800
|
MPa
|
ASTM D790 |
|
-- 6
|
6300
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
-- 6, 7
|
150
|
MPa
|
ISO 178 |
|
屈服, 50.0 mm 跨距 5
|
145
|
MPa
|
ASTM D790 |
|
弯曲应变 - at Break 8
|
3.0
|
%
|
ISO 178 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度
|
|||
|
-30°C 9
|
5.0
|
kJ/m²
|
ISO 179/1eA |
|
-30°C
|
9.0
|
kJ/m²
|
ISO 179/2C |
|
23°C 9
|
6.0
|
kJ/m²
|
ISO 179/1eA |
|
23°C
|
9.0
|
kJ/m²
|
ISO 179/2C |
|
简支梁无缺口冲击强度
|
|||
|
-30°C 9
|
40
|
kJ/m²
|
ISO 179/1eU |
|
-30°C
|
50
|
kJ/m²
|
ISO 179/2U |
|
23°C 9
|
40
|
kJ/m²
|
ISO 179/1eU |
|
23°C
|
55
|
kJ/m²
|
ISO 179/2U |
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
80
|
J/m
|
ASTM D256 |
|
0°C
|
80
|
J/m
|
ASTM D256 |
|
23°C
|
80
|
J/m
|
ASTM D256 |
|
-30°C 10
|
6.0
|
kJ/m²
|
ISO 180/1A |
|
0°C 10
|
7.0
|
kJ/m²
|
ISO 180/1A |
|
23°C 10
|
7.0
|
kJ/m²
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
-30°C
|
650
|
J/m
|
ASTM D4812 |
|
23°C
|
650
|
J/m
|
ASTM D4812 |
|
-30°C 10
|
35
|
kJ/m²
|
ISO 180/1U |
|
23°C 10
|
40
|
kJ/m²
|
ISO 180/1U |
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
65.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 3.20 mm
|
180
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
|
180
|
°C
|
ISO 75-2/Bf |
|
1.8 MPa, 未退火, 3.20 mm
|
120
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
|
120
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
200
|
°C
|
ASTM D1525 11, ISO 306/A50 11 |
|
--
|
145
|
°C
|
ASTM D1525 12, ISO 306/B120, ISO 306/B50 |
|
Ball Pressure Test (123 到 127°C)
|
通过
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 40°C
|
4.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : -40 到 40°C
|
2.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
流动 : 23 到 60°C
|
4.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
流动 : 23 到 80°C
|
4.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
流动 : 23 到 150°C
|
2.4E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : -40 到 40°C
|
1.0E-4
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : -40°C
|
6.9E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : 23 到 60°C
|
1.0E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : 23 到 80°C
|
1.0E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : 23 到 150°C
|
1.1E-4
|
cm/cm/°C
|
ISO 11359-2 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
> 1.0E+16
|
ohms
|
IEC 60093 |
|
体积电阻率
|
|||
|
--
|
> 1.0E+15
|
ohms·cm
|
ASTM D257 |
|
--
|
> 1.0E+16
|
ohms·cm
|
IEC 60093 |
|
介电强度
|
|||
|
0.800 mm, in Oil
|
31
|
kV/mm
|
ASTM D149 |
|
1.60 mm, in Oil
|
28
|
kV/mm
|
ASTM D149 |
|
3.20 mm, in Oil
|
16
|
kV/mm
|
ASTM D149 |
|
0.800 mm, 在油中
|
31
|
kV/mm
|
IEC 60243-1 |
|
1.60 mm, 在油中
|
28
|
kV/mm
|
IEC 60243-1 |
|
3.20 mm, 在油中
|
16
|
kV/mm
|
IEC 60243-1 |
|
介电常数
|
|||
|
1 MHz
|
3.30
|
|
ASTM D150, IEC 60250 |
|
50 Hz
|
3.10
|
|
IEC 60250 |
|
60 Hz
|
3.10
|
|
IEC 60250 |
|
100 Hz
|
3.30
|
|
IEC 60250 |
|
耗散因数
|
|||
|
1 MHz
|
0.014
|
|
ASTM D150, IEC 60250 |
|
50 Hz
|
1.0E-3
|
|
IEC 60250 |
|
60 Hz
|
1.0E-3
|
|
IEC 60250 |
|
100 Hz
|
1.0E-3
|
|
IEC 60250 |
|
漏电起痕指数
|
IEC 60112 | ||
|
--
|
250
|
V
|
|
|
解决方案 B
|
100
|
V
|
|
|
高电弧燃烧指数(HAI) 13
|
PLC 0
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 0
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
1.5 mm
|
HB
|
|
|
|
3.0 mm
|
HB
|
|
|
|
灼热丝易燃指数
|
IEC 60695-2-12 | ||
|
1.0 mm
|
750
|
°C
|
|
|
2.0 mm
|
850
|
°C
|
|
|
极限氧指数
|
23
|
%
|
ISO 4589-2 |
| 充模分析 |
额定值
|
单位制
|
测试方法
|
|
熔体粘度 (260°C, 1500 sec^-1)
|
215
|
Pa·s
|
ISO 11443 |
| 补充信息 |
额定值
|
单位制
|
测试方法
|
|
填充物
|
20
|
%
|
ASTM D229 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
110 到 120
|
°C
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料斗温度
|
40 到 60
|
°C
|
|
|
料筒后部温度
|
230 到 245
|
°C
|
|
|
料筒中部温度
|
240 到 255
|
°C
|
|
|
料筒前部温度
|
245 到 265
|
°C
|
|
|
射嘴温度
|
240 到 260
|
°C
|
|
|
加工（熔体）温度
|
250 到 270
|
°C
|
|
|
模具温度
|
40 到 100
|
°C
|
| 备注 |
| 1UL 黄卡含有 UL 验证的易燃性和电气特性。UL Prospector 持续努力在 Prospector 中将黄卡链接至单个塑料材料，然而此列表可能未包括所有相应链接。重要的是，我们对 Prospector 中找到的这些黄卡和塑料材料之间的关联进行验证。如需完整的黄卡列表，请访问 UL 黄卡搜索。 |
| 2Tensile Bar |
| 35.0 mm/min |
| 4类型 1, 5.0 mm/min |
| 51.3 mm/min |
| 62.0 mm/min |
| 7at Yield |
| 82 mm/min |
| 980*10*4 sp=62mm |
| 1080*10*4 mm |
| 11速率 A (50°C/h), 压 力1 (10N) |
| 12速率 A (50°C/h), 载荷2 (50N) |
| 13Surface |
点击下载VALOXVX5022物性表：
备注：以上数据表中的信息由 HuasuStar - 华塑之星 从该材料的生产商处获得。HuasuStar - 华塑之星 尽最大努力确保此数据的准确性。 但是 HuasuStar - 华塑之星 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料生产商进行验证。