VALOX 553U|PBT 553U|沙特基础工业公司|VALOX 553U物性表|553U PBT塑胶原料|SABIC代理商
点击下载VALOX 553U物性表：
VALOX™ FR Resin 553U
聚碳酸酯+PBT
SABIC
产品说明:
VALOX 553U is a 30% glass filled, UV stabilized flame retardant Polybutylene Terephthalate/Polycarbonate (PBT/PC) injection moldable grade. It has excellent chemical resistance and a UL94V0@0.86mm and 5VA@2.31mm flame rating. This is a good candidate for applications needing reduced shrinkage/warpage including appliance handles, spotlights, electric motors, and pump housings
VALOX™ FR Resin 553U
聚碳酸酯+PBT
SABIC
产品说明:
VALOX 553U is a 30% glass filled, UV stabilized flame retardant Polybutylene Terephthalate/Polycarbonate (PBT/PC) injection moldable grade. It has excellent chemical resistance and a UL94V0@0.86mm and 5VA@2.31mm flame rating. This is a good candidate for applications needing reduced shrinkage/warpage including appliance handles, spotlights, electric motors, and pump housings
|
用途
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.58
|
g/cm³
|
ASTM D792 |
|
特定体积
|
0.630
|
cm³/g
|
ASTM D792 |
|
收缩率
|
内部方法 | ||
|
垂直 : 1.50 到 3.20 mm
|
0.40 到 0.60
|
%
|
|
|
流动 : 1.50 到 3.20 mm
|
0.30 到 0.50
|
%
|
|
|
垂直 : 3.20 到 4.60 mm
|
0.60 到 0.90
|
%
|
|
|
流动 : 3.20 到 4.60 mm
|
0.50 到 0.80
|
%
|
|
|
吸水率 (24 hr)
|
0.070
|
%
|
ASTM D570 |
|
室外适用性
|
f1
|
|
UL 746C |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度 (R 级)
|
118
|
|
ASTM D785 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度 2 (断裂)
|
110
|
MPa
|
ASTM D638 |
|
弯曲模量 3 (50.0 mm 跨距)
|
6890
|
MPa
|
ASTM D790 |
|
弯曲强度 3 (断裂, 50.0 mm 跨距)
|
179
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度 (23°C)
|
85
|
J/m
|
ASTM D256 |
|
无缺口悬臂梁冲击 (23°C)
|
640
|
J/m
|
ASTM D4812 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
0.45 MPa, 未退火, 6.40 mm
|
204
|
°C
|
|
|
1.8 MPa, 未退火, 6.40 mm
|
160
|
°C
|
|
|
线形热膨胀系数 - 流动
|
ASTM E831 | ||
|
-40 到 40°C
|
2.2E-5
|
cm/cm/°C
|
|
|
60 到 138°C
|
2.2E-5
|
cm/cm/°C
|
|
|
RTI Elec
|
125
|
°C
|
UL 746 |
|
RTI Imp
|
110
|
°C
|
UL 746 |
|
RTI
|
125
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
4.3E+16
|
ohms·cm
|
ASTM D257 |
|
介电强度
|
ASTM D149 | ||
|
1.60 mm, in Oil
|
26
|
kV/mm
|
|
|
3.20 mm, in Air
|
19
|
kV/mm
|
|
|
介电常数
|
ASTM D150 | ||
|
100 Hz
|
3.80
|
|
|
|
1 MHz
|
3.70
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
100 Hz
|
2.0E-3
|
|
|
|
1 MHz
|
0.020
|
|
|
|
耐电弧性 4
|
PLC 6
|
|
ASTM D495 |
|
相比耐漏电起痕指数(CTI)
|
PLC 3
|
|
UL 746 |
|
高电弧燃烧指数(HAI) 5
|
PLC 3
|
|
UL 746 |
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 1
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
0.9 mm
|
V-0
|
|
|
|
2.3 mm
|
5VA
|
|
|
|
极限氧指数
|
37
|
%
|
ASTM D2863 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
120
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 80
|
%
|
|
|
料筒后部温度
|
240 到 255
|
°C
|
|
|
料筒中部温度
|
245 到 260
|
°C
|
|
|
料筒前部温度
|
250 到 265
|
°C
|
|
|
射嘴温度
|
245 到 260
|
°C
|
|
|
加工（熔体）温度
|
250 到 265
|
°C
|
|
|
模具温度
|
65 到 90
|
°C
|
|
|
背压
|
0.300 到 0.700
|
MPa
|
|
|
螺杆转速
|
50 到 80
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.038
|
mm
|
备注：以上数据表中的信息由 HuasuStar - 华塑之星 从该材料的生产商处获得。HuasuStar - 华塑之星 尽最大努力确保此数据的准确性。 但是 HuasuStar - 华塑之星 对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料生产商进行验证。