EXTEM/TPI VH1003F,VH1003F物性表，SABIC，沙伯基础创新塑料有限公司
EXTEM™ Resin VH1003F - Asia
聚醚酰亚胺
SABIC
Product Description:
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815. Global Food Contact Approvals. Resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited.
聚醚酰亚胺
SABIC
Product Description:
Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant and also halogen free according VDE/DIN 472 part 815. Global Food Contact Approvals. Resin is a Dual-use item and is subject to export control restrictions under both U.S. 15 CFR 774 and Annex I of Reg. (EC) 428/2009 as ECCN 1C008. Diversion contrary to law is prohibited.
|
搜索 UL 黄卡
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.30
|
g/cm³
|
ASTM D792, ISO 1183 |
|
熔流率（熔体流动速率） (367°C/6.6 kg)
|
16
|
g/10 min
|
ASTM D1238 |
|
熔融体积流量（MVR） (360°C/5.0 kg)
|
8.0
|
cm³/10min
|
ISO 1133 |
|
收缩率
|
内部方法 | ||
|
流动 1
|
0.50 到 0.70
|
%
|
|
|
垂直 : 3.20 mm
|
0.50 到 0.70
|
%
|
|
|
流动 : 3.20 mm
|
0.50 到 0.70
|
%
|
|
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
1.8
|
%
|
|
|
平衡, 23°C, 50% RH
|
0.60
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
球压硬度 (H 358/30)
|
140
|
MPa
|
ISO 2039-1 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
-- 2
|
3510
|
MPa
|
ASTM D638 |
|
--
|
3110
|
MPa
|
ISO 527-2/1 |
|
抗张强度
|
|||
|
屈服 3
|
96.0
|
MPa
|
ASTM D638 |
|
屈服
|
95.0
|
MPa
|
ISO 527-2/5 |
|
断裂 3
|
96.0
|
MPa
|
ASTM D638 |
|
断裂
|
78.0
|
MPa
|
ISO 527-2/5 |
|
伸长率
|
|||
|
屈服 3
|
6.0
|
%
|
ASTM D638 |
|
屈服
|
8.5
|
%
|
ISO 527-2/5 |
|
断裂 3
|
50
|
%
|
ASTM D638 |
|
断裂
|
50
|
%
|
ISO 527-2/5 |
|
弯曲模量
|
|||
|
50.0 mm 跨距 4
|
3170
|
MPa
|
ASTM D790 |
|
-- 5
|
3080
|
MPa
|
ISO 178 |
|
弯曲应力
|
|||
|
-- 5, 6
|
123
|
MPa
|
ISO 178 |
|
屈服, 100 mm 跨距 7
|
155
|
MPa
|
ASTM D790 |
|
断裂, 50.0 mm 跨距 4
|
159
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁无缺口冲击强度 8
|
ISO 179/1eU | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-30°C
|
74
|
J/m
|
ASTM D256 |
|
23°C
|
69
|
J/m
|
ASTM D256 |
|
-30°C 9
|
5.0
|
kJ/m²
|
ISO 180/1A |
|
23°C 9
|
4.0
|
kJ/m²
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
23°C
|
无断裂
|
|
ASTM D4812, ISO 180/1U |
|
-30°C 9
|
无断裂
|
|
ISO 180/1U |
|
装有测量仪表的落镖冲击 (23°C, Total Energy)
|
33.0
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
|||
|
0.45 MPa, 未退火, 6.40 mm
|
237
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 3.20 mm
|
217
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 6.40 mm
|
230
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9
|
228
|
°C
|
ISO 75-2/Af |
|
维卡软化温度
|
|||
|
--
|
242
|
°C
|
ASTM D1525 10, ISO 306/B50 10 |
|
--
|
238
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (123 到 127°C)
|
通过
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|||
|
流动 : -40 到 150°C
|
5.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
流动 : 23 到 150°C
|
5.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
垂直 : -40 到 150°C
|
5.0E-5
|
cm/cm/°C
|
ASTM E831 |
|
垂直 : 23 到 150°C
|
5.0E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
导热系数
|
0.22
|
W/m/K
|
ASTM E1530 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
介电强度 (3.20 mm, in Oil)
|
17
|
kV/mm
|
ASTM D149 |
|
介电常数
|
ASTM D150 | ||
|
100 Hz
|
3.41
|
|
|
|
1 kHz
|
3.41
|
|
|
|
耗散因数
|
IEC 60250 | ||
|
50 Hz
|
0.025
|
|
|
|
60 Hz
|
0.025
|
|
|
|
100 Hz
|
8.0E-3
|
|
|
|
1 kHz
|
1.0E-3
|
|
|
|
1 MHz
|
7.0E-3
|
|
|
|
漏电起痕指数
|
175
|
V
|
IEC 60112 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
灼热丝易燃指数 (3.2 mm)
|
960
|
°C
|
IEC 60695-2-12 |
|
热灯丝点火温度 (3.0 mm)
|
850
|
°C
|
IEC 60695-2-13 |
|
极限氧指数
|
45
|
%
|
ISO 4589-2 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
透射率 (2540 µm)
|
58.0
|
%
|
ASTM D1003 |
|
雾度 (2540 µm)
|
2.00
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
150
|
°C
|
|
|
干燥时间
|
4.0 到 6.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
360 到 380
|
°C
|
|
|
料筒中部温度
|
370 到 395
|
°C
|
|
|
料筒前部温度
|
380 到 405
|
°C
|
|
|
射嘴温度
|
375 到 400
|
°C
|
|
|
加工（熔体）温度
|
380 到 405
|
°C
|
|
|
模具温度
|
135 到 165
|
°C
|
|
|
背压
|
0.300 到 0.700
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
|
| 注射说明 | |||
|
Injection Molding Parameters
|
|||
| 备注 |
| 1Tensile Bar |
| 25.0 mm/min |
| 3类型 1, 5.0 mm/min |
| 41.3 mm/min |
| 52.0 mm/min |
| 6at Yield |
| 72.6 mm/min |
| 880*10*4 sp=62mm |
| 980*10*4 mm |
| 10速率 A (50°C/h), 载荷2 (50N) |